What are the effects of injection mold temperature on injection molded parts?

There are many factors affecting the cooling of the injection mold, such as the shape of the plastic part and the design of the parting surface, the type, temperature, and flow rate of the cooling medium, the geometric parameters and spatial arrangement of the cooling pipe, the mold material, the temperature of the melt, the ejection temperature and mold temperature required for the plastic part, the interaction of the heat cycle between the plastic part and the mold, etc.

1.  Low mold temperature can reduce the molding shrinkage of plastic parts.
2.  Uniform mold temperature, short cooling time and fast injection speed can reduce the warpage of plastic parts.
3.  For crystalline polymers, increasing the mold temperature can stabilize the dimensions of the molded part and avoid the post-crystallization phenomenon, but it will lead to a longer molding cycle and the defect of the brittle molded part.
4.  As the crystallinity of crystalline polymers increases, the stress cracking resistance of the plastic decreases, so it is advantageous to lower the mold temperature. However, for high viscosity amorphous polymers, it is advantageous to increase the mold temperature and mold filling speed to reduce the replenishment time because the stress cracking resistance is directly related to the internal stress of the molded part.
5.  Increasing the mold temperature can improve the surface quality of the plastic parts. Mold temperature is determined during the injection molding process, mold temperature directly affects the plastic filling, plastic part setting, molding cycle, and plastic part quality.

The temperature of the mold depends on the crystallinity of the plastic, the size and structure of the part, the performance requirements, and other process conditions such as melt temperature, injection speed, injection pressure, and molding cycle.

For amorphous polymers, the melt is injected into the mold cavity and cured as the temperature decreases, but there is no phase change, and the mold temperature mainly affects the viscosity of the melt, i.e., the mold filling rate. Therefore, for amorphous plastics with low and medium melt viscosity, such as polystyrene and cellulose acetate, the cooling time can be shortened by using lower mold temperature.